SEMICOSIL® 962 TC/2K
|
Property
|
Condition
|
Value
|
Method
|
|---|---|---|---|
| Color of Component A | - | red | - |
| Color of Component B | - | white | - |
| Density (Component A) | 23 °C | 3.1 g/cm³ | DIN EN ISO 1183-1 A |
| Density (Component B) | 23 °C | 3.1 g/cm³ | DIN EN ISO 1183-1 A |
| Viscosity, dynamic (Cone-plateviscosimeter) | 23 °C | 150000 mPa·s | ISO 3219, D = 10 1/s |
| Viscosity, dynamic (Cone-plateviscosimeter) | 23 °C | 150000 mPa·s | ISO 3219, D = 10 1/s |
|
Property
|
Condition
|
Value
|
Method
|
|---|---|---|---|
| Viscosity, dynamic of mix | 23 °C | 150000 mPa·s | ISO 3219, D = 10 1/s |
| Platinum catalyst in component | - | A | - |
| Mix ratio[1] | - | 1 : 1 | - |
| Pot Life (up to 1000000 mPa s) | 23 °C | 60 min | - |
Cured for 10 min at 165 °C.
|
Property
|
Condition
|
Value
|
Method
|
|---|---|---|---|
| Color | - | red | - |
| Density in water | 23 °C | 3.1 g/cm³ | DIN EN ISO 1183-1 A |
| Hardness Shore 00 | - | 50 | ASTM D 2240 |
| Volume resistivity | - | > 10¹³ Ohmcm | - |
| Dielectric strength | - | 7 kV/mm | - |
| Content siloxane D4-D8 | - | < 350 ppm | NSCG012 |
| Flame Rating vertical test | - | V-O | Internal test acc. UL94 |
| Heat capacity | 30 °C | 1 J/gK | - |
| Maximum particle size | - | 90 µm | - |
| Thermal conductivity | - | 3 W/m.K | - |
All the information provided is in accordance with the present state of our knowledge. Nonetheless, we disclaim any warranty or liability whatsoever and reserve the right, at any time, to effect technical alterations. The information provided, as well as the product's fitness for an intended application, should be checked by the buyer in preliminary trials. Contractual terms and conditions always take precedence. This disclaimer of warranty and liability also applies particularly in foreign countries with respect to third parties' rights.
| Colour: | Red |
|---|---|
| Max. temp. °C: | 180°C |
| Properties: | Thermally conductive |
| Silicone product groups: | Potting compounds |
| Thermal conductivity: | 3,0 [W/mK] |
| Viscosity [mPa·s] D=0.5–1 1/s: | Non-slump |
Zubehör
- Flame coating device
- Effective and cost-effective
- Can be used for almost all materials
- Gentle on materials in terms of temperature
- Adhesion promoter, for addition-curing silicone
- Coating techniques such as dipping, brushing or spraying
- Free from toluene and other aromatic solvents