ELASTOSIL® M 4645 A/B
Product number:
60080755
Product information "ELASTOSIL® M 4645 A/B"
Properties Uncured
These figures are only intended as a guide and should not be used in preparing specifications.
|
Property
|
Condition
|
A
|
B
|
Method
|
|---|---|---|---|---|
| Color | - | translucent | colorless | - |
| Density | 23 °C | 1.08g/cm³ | 0.97 g/cm³ | DIN EN ISO 2811-1 |
| Viscosity, dynamic after stirring | 23 °C | 50000 mPa·s | 3500mPa·s | ISO 3219 |
Properties Catalyzed A+B
|
Property
|
Condition
|
Value
|
Method
|
|---|---|---|---|
| Viscosity, dynamic | 23 °C | 35000 mPa·s | ISO 3219 |
| Mix ratio[1] | - | 10 : 1 | A : B |
| Pot Life (up to 60000 mPas) | 23 °C | 80 min | DIN EN ISO 2555 |
| Curing time tack free | - | 12 h | - |
1 pbw These figures are only intended as a guide and should not be used in preparing specifications.
Properties Cured
curing conditions: 24 h / 23 °C
curing conditions: 24 h / 23 °C
|
Property
|
Condition
|
Value
|
Method
|
|---|---|---|---|
| Color | - | translucent | - |
| Density in water | 23 °C | 1.06g/cm³ | ISO 2781 |
| Tear strength | - | > 28 N/mm | ASTM D 624 B |
| Hardness Shore A | - | 40 | ISO 868 |
| Tensile strength | - | 5 N/mm² | ISO 37 |
| Elongation at break | - | 330 % | ISO 37 |
| Linear shrinkage | - | < 0.1 % | - |
Disclaimer
All the information provided is in accordance with the present state of our knowledge. Nonetheless, we disclaim any warranty or liability whatsoever and reserve the right, at any time, to effect technical alterations. The information provided, as well as the product's fitness for an intended application, should be checked by the buyer in preliminary trials. Contractual terms and conditions always take precedence. This disclaimer of warranty and liability also applies particularly in foreign countries with respect to third parties' rights.
Properties "ELASTOSIL® M 4645 A/B"
| Properties: | Resistant to casting resins |
|---|---|
| Shore A: | 40 |
| Silicone product groups: | Silicone additives |
| Silicone system: | RTV-2 addition-curing |