ELASTOSIL® M 4601 A/B
Product information "ELASTOSIL® M 4601 A/B"
Properties Uncured
These figures are only intended as a guide and should not be used in preparing specifications.
|
Property
|
Condition
|
A
|
B
|
Method
|
|---|---|---|---|---|
| Color | - | white | reddish brown | - |
| Density | 23 °C | 1.14 g/cm³ | 1.01 g/cm³ | DIN EN ISO 2811-1 |
| Viscosity, dynamic after stirring | 23 °C | 15000 mPa·s | 800 mPa·s | ISO 3219 |
Properties Catalyzed A+B
|
Property
|
Condition
|
Value
|
Method
|
|---|---|---|---|
| Viscosity, dynamic | 23 °C | 10000 mPa·s | ISO 3219 |
| Mix ratio[1] | - | 9 : 1 | A : B |
| Pot Life up to 60,000 mPa s | 23 °C | 90 min | DIN EN ISO 2555 |
| Curing time tack-free | - | 12 h | - |
1 pbw. These figures are only intended as a guide and should not be used in preparing specifications.
Properties Cured
Curing conditions: 24 h / 23 °C
These figures are only intended as a guide and should not be used in preparing specifications.
| Property | Condition | Value | Method |
|---|---|---|---|
| Color | - | reddish brown | - |
| Density in water | 23 °C | 1.13 g/cm³ | ISO 2781 |
| Tear strength | - | > 30 N/mm | ASTM D 624 B |
| Hardness Shore A | - | 28 | ISO 868 |
| Tensile strength | - | 6.5 N/mm² | ISO 37 |
| Elongation at break | - | 700 % | ISO 37 |
| Linear shrinkage | - | < 0.1 % | - |
Disclaimer
All the information provided is in accordance with the present state of our knowledge. Nonetheless, we disclaim any warranty or liability whatsoever and reserve the right, at any time, to effect technical alterations. The information provided, as well as the product's fitness for an intended application, should be checked by the buyer in preliminary trials. Contractual terms and conditions always take precedence. This disclaimer of warranty and liability also applies particularly in foreign countries with respect to third parties' rights.
Properties "ELASTOSIL® M 4601 A/B"
| Colour: | Reddish brown |
|---|---|
| Elongation at break: | 700 % |
| Max. temp. °C: | 200°C |
| Properties: | Food contact, High mechanical strength, Resistant to casting resins |
| Shore A: | 28 |
| Silicone product groups: | Mould-making compounds |
| Silicone system: | RTV-2 addition-curing |
| Tensile strength: | 6.5 N/mm² |
| Viscosity [mPa·s] D=0.5–1 1/s: | 10'000 - 20'000 |